元素的氢脆测试潜艇雷达(他)rmines the performance of materials in a corrosive environment under the influence of the tensile stress by evaluating the material’s ductility as a result of hydrogen absorption. The tests may be carried out according to ASTM F519 standard for many industries includingEnergy,Aerospace和www.yabo88.com .
当金属在电镀工艺期间或在服务环境中的腐蚀的结果时发生氢气脆化。这使得金属失去延展性和韧性并变脆,导致静态负荷下的过早失效。
There are two types of Hydrogen Embrittlement (HE): Internal HE, which occurs when the hydrogen enters metal during forming, coating, plating, cleaning, and finishing operations; and Environmental HE, resulting from hydrogen being absorbed from the environment.
元件performs HE testing for coating and plating processes that can cause hydrogen embrittlement in steels, and on the metals in simulated service environments. Our deep knowledge of corrosion testing and years of experience means that we know the challenges of assessing hydrogen-related damage in many industries.
ASTM F519 test method
元件performs mechanical hydrogen embrittlement testing according to ASTM F519. The test specification outlines the use of Sustained Load Testing (SLT) to measure the possibility of hydrogen embrittlement in steel materials by applying uniaxial tension for up to 200 hours.
Additionally, ASTM F519 provides guidance for evaluating the processes of surface preparation, pretreatments, and the plating/coating of steel parts.
Galvanically Induced Hydrogen Stress Cracking (GHSC)
The presence of hydrogen (introduced via corrosion) in a metal may result in reduced ductility and increased susceptibility to cracking in the presence of tensile stress (applied and /or residual). Element’s GHSC testing helps evaluate the hydrogen embrittlement sustainability of the corrosion resistant products and metal materials, when galvanically coupled, as the cathode, to another metal (carbon steel). We perform testing in accordance toNACE MR0175 / ISO 15156.
Hydrogen Induced Stress Cracking (HISC)
Subsea Oil & Gas production equipment is exposed to severe conditions which have led to a number of failures of Corrosion Resistant Alloys (CRAs). Our hydrogen embrittlement testing labs can carry out HISC testing of nickel alloys and duplex stainless steels, widely used in subsea components, to investigate how hydrogen influences materials’ behavior under mechanical stress.
For more information about how we perform Hydrogen Embrittlement (HE) Testing, or to request a quote,contact us today.
Related Services
As a recognized world- leader in the provision of corrosion testing services, Element performs a number of testing services related to hydrogen embrittlement.
Hydrogen Induced Cracking (HIC) Testing
根据NACE TM0284,Element的HIC测试评估酸性环境中氢诱导裂缝的材料敏感性。
Read More
Stress Corrosion Cracking (SCC) Testing
元素的应力腐蚀裂解(SCC)测试评估金属在拉伸应力和腐蚀下破裂破裂的易感性。
Read More
Slow Strain Rate Testing (SSRT)
元件’s Slow Strain Rate Testing (SSRT) uses Rippled SSRT methods to ensure the safety and reliability of metals.
Read More
making certain for nearly 190 years
更多来自元素
Corrosion Testing
元件’s corrosion testing laboratories provide complete corrosion testing services to many industries, including salt spray, cyclic corrosion, pitting testing, and more.
Read More
Sour Service Corrosion Testing
元件is one of a few ISO certified sour service labs in the world, providing sour service corrosion services for a variety of test types including NACE MR0175/ISO 15156.
Read More
亚慱体育怎么下载
Discover blog posts, articles, white papers, webinars, and advice from our world-leading testing, inspection, and certification experts.
元件Locations
了解更多关于我们的实验室 - 在哪里;他们拥有的独特功能以及如何帮助您解决您的技术和商业挑战。
FIND A LABORATORY